An Update of small shot for Smoothbores.
My last findings during researching lead shot had me puzzled. In George Washington's list of goods he ordered "Drop Shot". This was prior to the invention of the shot tower. Further searching has turned up a couple of interesting facts. (1) Prince Rupert's shot maker, & (2) Prince Rupert's experiment with glass. Prince Rupert melted glass & dropped some into a bucket of water, the result was known as Rupert's Drop. This glass droplet reminds me of the shape of a swan, & it made me wonder if there was any connection between this glass "drop" & the wrongly assumed shape of swan shot?!
It also made me wonder if the term "Rupert's Drop" had anything to do with the term "Drop Shot" used by George Washington. Certainly the method used in making "Rupert's Shot" could be termed "Drop Shot". Here then below is the information I have collected to date, I hope you find it of some interest & perhaps of use.
Keith.
Prince Rupert of the Rhine, inventor of Rupert's Shot & Rupert's Drop.
Rupert's Drop.
Drop Shot.
Markham noted the superiority of “haileshot or drop-shot”
#4 drop shot that replaced Rupert shot after 1784.
“It was made by pouring moulten lead through a brass colander held
over a bucket of water. The molten lead fell through the holes into the water
forming slightly oval dimpled shot. Rupert shot is frequently found at
Michilimackinac…Some of this shot still has tails, indicating that it was
possibly run at the fort,”
Craft industries at Fort Michilimackinac, 1715-1781,Lynn L. Morand,
Mackinac Historical Parks, Mackinac Island’ MI, 1994, pgs.40-43.
He also invented an improved method for manufacturing shot of
varying sizes in 1663, that was later retained by the scientist Robert
Hooke, one of Rupert's Royal Society friends during the period.[171]
The one great breakthrough in the history of shot making came in
1782, when a British plumber, William Watts of Bristol, received a patent for a
method to produce shot…
Good old WW was a Bristol plumber and in 1782 he discovered a way of
making perfect lead shot.
In 1782 an English plumber named William Watts saw possibility in
that. He realized that if he dropped molten lead far enough through the air,
it, too, would form into spheres. The surface tension of lead is a lot higher
than that of water, so it forms very perfect spheres indeed.
“If you want a scientific display of the dangers of pent-up stress, Prince
Rupert's drops are it. After the trauma of being dropped molten-hot into
a bucket of cold water, these glass balls, named for a 17th-century amateur scientist,”
Rupert's drops are it. After the trauma of being dropped molten-hot into
a bucket of cold water, these glass balls, named for a 17th-century amateur scientist,”
The above comment relates to drops of molten glass, but of course the
same man, Prince Rupert also designed the first Drop Shot by pouring
molten lead through a sieve into a bucket of water. This could explain
Washington’s use of the term Drop Shot before the shot tower was
invented.
Keith. 4/4/2016.
Lead shot was also found at the house sites in various sizes, and of
three basic manufacturing types. Rupert’s shot, which was typically
purchased, was made by pouring melted lead, fluxed with arsenic, through a
colander into tubs of water. The size of the holes in the colander determined
the size of the shot. Rupert’s shot has a small characteristic dimple on it.
Like fish hooks, lead shot was not sold with number sizes as it is today, but
with names corresponding to their intended game. In 18th-century Connecticut,
merchants typically advertised such shot types as “bird,” “duck,” “geese” and
“swan.” Some hunters made their own shot, which they cast into specially-made
shot molds called gang molds. The molds were manufactured from brass or were
homemade, carved out of local soapstone (steatite). Shot was also produced by a
laborious process which involved pounding lead into long rectangular blanks and
then cutting off small cubes of the desired shot size. The edges of this type
of “tumbled shot” were then rounded by rolling them in sand or ash.25
“FIGURE 18 Lead shot and sprue a-f, Rupert shot with characteristic ‘ dimples’, g-h, cast shot, showing mold seams
and sprue nibs, m-p cast musketballs (note teeth marks on p), ), q-s, sprue
from small cast shot, t, shot still attached to sprue”. (image of shot at url
link. Keith.)
Lead Ball and Shot Production.
A final activity related to
firearms was the production of shot and musketballs. Judging from the
accumulation of sprue in the workshop refuse, the majority of early shot was
laboriously cast in gang molds (Figure I8g-1). Rupert shot was also
present, though in lesser quantities (Figure 18a-f). The two types can usually
be distinguiished by the seam and cut-off marks on the cast shot, and the
dimple characteristic of the Rupert process (Hamilton 1980: 13 1-133). This
latter form was made by dropping lead through a heated colander into a pan of
water immediately below. The shot was then graded by sieving (Brown 1980:84).
Whether the Rupert shot was made on the site has not been determined, but the
size distributions of the two are roughly similar, and indicate that they were
functionally interchangeable (Figure 19). Apparently at least three or four
sizes of shot were used at the fort, but the smallest size, at 5 mm was the
most popular, probably for fowling pieces. A reversal in the relative
popularity of shot types occurs in all areas away from the workshop,
particularly the paving of the gateway outside the guard house, indicating
either that Rupert shot was not made at the workshop, or that it replaced cast
shot in Pentagoet 111 (Figure 20). Within buildings, of course, all exposed
Pentagoet I11 shot was melted in the destruction of the fort.
Maintenance and Fabrication at Fort Pentagoet 1635-1 654 Products of
an Acadian Armorer’s Workshop
To make small shot of different sizes; Communicated by
his Highness P.R.
Take Lead out of the Pig what quantity you please, melt it down, stir
and clear it with an iron Ladle, gathering together the blackish parts that
swim at top like scum, and when you see the colour of the clear Lead to be
greenish, but no sooner, strew upon it Auripigmentum powdered
according to the quantity of Lead, about as much as will lye upon a half Crown
piece will serve for eighteen or twenty pound weight of some sorts of Lead;
others will require more, or less. After the Auripigmentum is put in,
stir the Lead well, and the Auripigmentum will flame: when the flame
is over, take out some of the Lead in a Ladle having a lip or notch in the brim
for convenient pouring out of the Lead, and being well warmed amongst the
melted Lead, and with a stick make some single drops of Lead trickle out of the
Ladle into water in a Glass, which if they fall to be round and without tails,
there is Auripigmentum enough put in, and the temper of the heat is
right, otherwise put in more. Then lay two bars of Iron (or some more proper
Iron-tool made on purpose) upon a Pail of water, and place upon them a round
Plate of Copper, of the size and figure of an ordinary large Pewter or Silver
Trencher, the hollow whereof is to be about three inches over, the bottom lower
then the brims about half an inch, pierced with thirty, forty, or more small
holes; the smaller the holes are, the smaller the shot will be; and the brim is
to be thicker then the bottom, to conserve the heat the better.
The bottom of the Trencher being some four inches distant from the
water in the Pail, lay upon it some burning Coles, to keep the Lead melted upon
it. Then with the hot Ladle take Lead off the Pot where it stands melted, and
pour it softly upon the burning Coles over the bottom of the Trencher, and it
will immediately run through the holes into the water in small round drops.
Thus pour on new Lead still as fast as it runs through the Trencher till all be
done; blowing now and then the Coles with hand-Bellows, when the Lead in the
Trencher cools so as to stop from running.
While one pours on the Lead, another must, with another Ladle,
thrusted four or five inches under water in the Pail, catch from time to time
some of the shot, as it drops down, to see the size of it, and whether there be
any faults in it. The greatest care is to keep the Lead upon the Trencher in
the right degree of heat; if it be too cool, it will not run through the
Trencher, though it stand melted upon it; and this is to be helped by blowing
the Coals a little, or pouring on new Lead that is hotter: but the cooler the
Lead, the larger the Shot; and the hotter, the smaller; when it it too hot, the
drops will crack and fly; then you must stop pouring on new Lead, and let it
cool; and so long as you observe the right temper of the heat, the Lead will
constantly drop into very round Shot, without so much as one with a tail in
many pounds.
When all is done, take your Shot out of the Pail of water, and put it
in a Frying-pan over the fire to dry them, which must be done warily, still
shaking them that they melt not; and when they are dry you may separate the
small from the great, in Pearl Sives made of Copper or Lattin let into one
another, into as many sizes at you please. But if you would have your Shot
larger then the Trencher makes them, you may do it with a Stick, making them
trickle out of the Ladle, as hath been said.
If the Trencher be but toucht a very little when the Lead stops from
going through it, and be not too cool, it will drop again, but it better not to
touch it at all. At the melting of the Lead take care that there be no kind of
Oyl, Grease, or the like, upon the Pots, or Ladles, or Trencher.
The Chief cause of this Globular Figure of the Shot, seems to be the Auripigmentum;
for, as soon as it is put in among the melted Lead, it loses its shining
brightness, contracting instantly a grayish film or skin upon it, when you scum
it to make it clean with the Ladle. So that when the Air comes at the falling
drop of the melted Lead, that skin constricts them every where equally: but
upon what account, and whether this be the true cause, is left to further disquisition.
The Project Gutenberg eBook, Micrographia, by Robert Hooke. 17th
century.
Also: By R. HOOKE, Fellow of the Royal Society. First
published in 1665.
This is an image of Peter Goebel's interpretation of Prince Rupert's shot maker.
http://www.goosebay-workshops.com/Militaria
http://www.goosebay-workshops.com/Militaria
This is an image of a hunter shooting ducks on the water, using what was called a "stalking horse". The stalking horse was used as a moving blind so the hunter could move closer to the game.
More on Small Shot for Smoothbores.
5.7mm - 5.8mm diameter (o/all length of strip is 78mm)." River Thames find.
The above I suspect is swan shot. It is about the same size that I make myself for use in my fusil & pistol, about 5/16 th of an inch.
Author's pouch of swan shot.
The first "shot tower" was invented & patented by William Watts in 1782, so before that date, there must have been other method/s of producing shot for fowling purposes. All evidence so far points to the use of moulds, as sprues have been found, & only moulding produces such sprues. However, this is not to say that rough shot was not made from hammering out lead ball & cutting pieces of lead from the resulting small sheet of lead. This method certainly works as I have done it myself & would be a suitable method to use in the wilderness if there were a need.
I must also make it clear that the terms "swan shot" & "goose shot" refer to the size of the shot, not the appearance, or the method of production. The shot available at the time recieved the name of the particular animal for which it was best suited.
Shot.
During the early years of the colony each Englishman who planned to
emigrate to Virginia was advised to supply himself with the following
"Armes":
"One Armour compleat,
light.
One long Peece, five foot
or five and a halfe, neere
Musket bore.
One sword.
One bandaleere [a bandoleer
was a belt worn to carry the
cases which held the
powder charges].
Twenty pound of powder.
Sixty pound of shot or
lead, Pistoll and Goose shot."
Contemporary records indicate that hunting game birds and animals was
a
popular New World diversion. Such sport served a twofold purpose, as
it
offered recreation to the settler and helped provide food for his
table.
Parts of early fowling pieces and numerous lead birdshot (called
goose
or swan shot during the early years of the 17th century) have been
recovered.
In the ash and burned soil of this hearth area, lead casting sprues
for swan shot were found,
“every one shall be completely furnished with arms, a musket, a
sword, bandoleers, a rest, a pound of powder, 20 bullets fitted to their
musket, or 4 pound of pistol shot or swan shot at least.”101
Charles J. Hoadly, The Public records of the Colony of Connecticut (Hartford, 1857) V. 25, 26.
Charles J. Hoadly, The Public records of the Colony of Connecticut (Hartford, 1857) V. 25, 26.
A box of goose shot, 1-2 a box of swan shot.
New York merchant 1731.
History of New Paltz, New York and Its
Old Families (from 1678 to 1820
Hammered Slug Probably the most common slug is that created from
normal lead balls, which were modified by hammering to substantially reduce their caliber. The final shape, whether square, hexagonal or round in section depends
on the number of times they were hammered. The length of a slug is irrelevant
to the function of the bullet, being determined simply by the caliber of the
original ball and the intended final caliber. The caliber of the original
bullet can be determined by the weight.
http://www.heritagescience.ac.uk/Research_Projects/projects/Projectposters/Conservation_of_Battlefield_Archaeology_project_report_-_Appendix_3
http://www.heritagescience.ac.uk/Research_Projects/projects/Projectposters/Conservation_of_Battlefield_Archaeology_project_report_-_Appendix_3
Location: St. Augustine
|
Site: Fountain of Youth
|
Period: 1560 - 1570
|
Group: Military items
|
Description: Lead shot
|
|
"They [the Indians] have also their moulds to make shotte, of
all sorts, as Musket bullets, pistoll bullets, swane and gose shotte, and
smaler sorts;....."
Bradford, 1648. Plymouth plantation.
“with some flints, lead, swan-shot, and a barrel of gunpowder”.
Benjamin Franklin 1755. The Writings of Benjamin Franklin, Volume 4
The dropped shot ranged from 0.22 to 0.71 inches (5.54 to 17.94mm).
The cast shot ranged from 0.22 to 0.71 inches (5.54 to 17.94mm).
The presence of handfuls of casting sprues and lead fragments from
making swan shot….
Archaeological Pathways to Historic Site Development By Stanley South
Lead shot from the 'Bronze Bell' wreck, early 18th century
I have been unable to define the term "drop shot", as these lists pre date the use of William Watts shot tower.
From an English civil war site.
This is possibly a swan shot gang mould.
Various types of round shot made from stone, iron and lead found on board the 16th century carrack Mary Rose.
Lead shot assemblage from the 1650 attack on Castledonovan Castle, Co. Cork .
Lead shot from the 1601 English Lord Deputy's Siege Camp at Kinsale, Co. Cork.
Tuesday, 29 March 2016
My Original 18th Century Fire Steel Update.
Some of you may remember that I acquired an original 18th century
fire steel some time ago. I decided to add it to my equipment replacing the
copy that I had been using. I found however that the original did not spark as
well as the copy, so I re-hardened the steel in the fire. The results were no
better, but I decided to keep it & use it anyway. If that was the way it
was, then that is how I will use it.
I have seen in some videos copies of fire steels that shed an enormous amount of sparks as if they are coated with some radioactive material. There was such a product sold many years ago for coating the steel on a flintlock, but I think it was removed from sale!!!
Keith.
I have seen in some videos copies of fire steels that shed an enormous amount of sparks as if they are coated with some radioactive material. There was such a product sold many years ago for coating the steel on a flintlock, but I think it was removed from sale!!!
Keith.
Monday, 28 March 2016
Winter Solstice Masquerade Party.
The New England Colonial Living History Group 1680-1760 will be holding it's annual Winter Solstice masquerade Party on Saturday the 18th of June 2016.
TIME. Anytime after 4 pm though I doubt any food will be served before 6pm.
FOOD. Probably pumpkin soup & bread at least. Bring a "plate" if you wish & something to put your soup in.
PLACE. Linstock House garden in Wychwood Forest.
WHO. Members & invited friends.
DRESS. Pre-mid 18th century.
ENTRY FEE. Free.
BYOG. Bring your own drinking vessel please. Wine bottles are acceptable but beer bottles are not.
There will be children present so mind your language & your behavour please.
NO GUNS!
Swords are allowed if they are a part of your dress, but NO sword play! (Be extremely careful. DO NOT let some idiot handle your sword!!!)
Keith.
Keith.
R.S.V.P. Keith at: historicaltrekker@gmail.com
Subscribe to:
Posts (Atom)